BRIDGE BEARING EPOXY

 

 

Product Characteristics

• Good thixotropic, easy to scrape;

• Strength increasing quickly, which will reduce the padding setting time and greatly improve the construction efficiency and equipment turnover;

• -20℃~40℃ large curing temperature range, better for outdoor and cold area application;

• Good curing performance, high compressive strength and bonding strength, good toughness and impact resistance, good aging and medium resistance (acid, alkali and water etc.)

Product Characteristics

• Good thixotropic, easy to scrape;

• Strength increasing quickly, which will reduce the padding setting time and greatly improve the construction efficiency and equipment turnover;

• -20℃~40℃ large curing temperature range, better for outdoor and cold area application;

• Good curing performance, high compressive strength and bonding strength, good toughness and impact resistance, good aging and medium resistance (acid, alkali and water etc.)

Application Range

• Repairing and leveling of bridge bearing pad stone.

• Making the surface flat but not smooth, letting the top surface elevation accuracy, making the pedestal bearing surface under fully behind the bearing pad on the stone and eliminate the phenomenon of local edge escapes.

• At the same time, by using our HM-Q2Z leveling adhesive, the two edges bearing pad stones under one beam or the top of the bearing pad stone on the abutment at the same elevation in horizontal, this will avoid bias, initial shear and uneven force.

Application Range

• Repairing and leveling of bridge bearing pad stone.

• Making the surface flat but not smooth, letting the top surface elevation accuracy, making the pedestal bearing surface under fully behind the bearing pad on the stone and eliminate the phenomenon of local edge escapes.

• At the same time, by using our HM-Q2Z leveling adhesive, the two edges bearing pad stones under one beam or the top of the bearing pad stone on the abutment at the same elevation in horizontal, this will avoid bias, initial shear and uneven force.

 

 

 
Technical Parameters
HM-Q2Z BEARING PAD STONE LEVELING ADHESIVE
AppearancePart A: Viscous Paste
Part B: Viscous Paste
Mixture Ratio2:1
Operation time, 25℃≥40min
Finger touch dry time, 25℃≥2h
Compressive strength, MPa≥65
Bending strength, MPa≥50